STRUCTURAL, FERROELECTRIC AND PIEZOELECTRIC PROPERTIES OF PbTiO3-MODIFIED COMPLEX 0.6Ba(Ti0.8Zr0.2)O3-0.4(Ba0.7Ca0.3)TiO3 CERAMICS

  • Nguyễn Huu Lam
  • Nguyen Hoang Thoan
  • Luong Thi Kim Phuong
  • Nguyen Xuan Duong
  • Luong Huu Bac
  • Dang Duc Dung
Từ khóa: Ba(Ti0.8Zr0.2)O3, (Ba0.7Ca0.3)TiO3, lead-based ferroelectric, lead-free ferroelectric, PbTiO3.

Tóm tắt

In this paper, the structural and ferroelectric properties of PbTiO3-modified 0.6Ba(Ti0.8Zr0.2)O3-0.4(Ba0.7Ca0.3)TiO3 ceramics are reported. The nonlinear electric polarization is observed at room temperature in 0.6Ba(Ti0.8Zr0.2)O3-0.4(Ba0.7Ca0.3)TiO3 and remained after the introduction of PbTiO3. With increasing the PbTiO3 concentration to 7 mol.%, high electrical remanent polarization of 13.11 µC/cm2 is achieved. The large strain and Smax/Emax values were also obtained in PbTiO3-modified compounds, where the highest piezoelectric coefficient values were estimated at around 642 pm/V for 3 mol.% PbTiO3-addition into 0.6Ba(Ti0.8Zr0.2)O3-0.4(Ba0.7Ca0.3)TiO3 compounds. We expected that the ceramics prepared in our study might be a suitable candidate for applications in electronic devices.

điểm /   đánh giá
Phát hành ngày
2024-03-26