SYNTHESIS OF REDUCED GRAPHENE OXIDE - Mn0.8Zn0.2Fe2O4 - POROUS POLYANILINE NANOCOMPOSITE MATERIALS FOR EFFECTIVE MICROWAVE ABSORPTION IN X-BAND

  • Nguyen Vu Tung Le Quy Don Technical University
  • Tran Quang Dat Le Quy Don Technical University
  • Nguyen Tran Ha Le Quy Don Technical University
  • Nguyen Thanh Nam
  • Do Quoc Hung Le Quy Don Technical University
Từ khóa: Ferrite, graphene, polyaniline, absorber

Tóm tắt

In this paper, a composite of reduced graphene oxide (RGO), manganese/zinc ferrite (Mn0.8Zn0.2Fe2O4 - MZF) nanoparticles, and porous polyaniline (PANI) was successfully synthesized to improve microwave absorption properties exclusively in X-band. The experimental results demonstrate that the synthesized ternary composite had RGO nanosheets decorated mostly with MZF nanoparticles, and porous PANI was uniformly coated onto the surface of RGO-MZF. The strong reflection loss value of -60.4 dB at 10 GHz and wide effective bandwidth are effectively achieved with the sample which had thicknesses of 2 mm and contained 33 weight % of product. The marked display of the microwave absorption properties of this composite was associated with their notable structure.

điểm /   đánh giá
Phát hành ngày
2021-05-10
In ra
Tập. 15 Số. 05 (2020)
Chuyên mục
BAI BAO KHOA HOC