Method for decrease in spliting and filling defect of nickel membrance fomed in inert titane electrode face into electroplating process.

Abstract

The experiments producing nickel by the way of electrolyzing nickel sulfate were resulted. The researches had been conducted with the concentration of NiSO₄.7H2O solution about 200 g/l, electric current density about 5 A/dm² and electric potential about 5 V. The electrolyse of nickel sulfate had been Rained some thin nickel plates on the surface of inert titanium cathodes. The results showed that the peeling & cracking places have a distribution of large amount of rough inclusions with grain sizes from 5 to 10 µm. In the edges of thin nickel plates there were high irregular electric current density, therefore the thickness of plate is also different leading to the difference of surface tension in thin plate mC1rgins and making crack of nickel plate margin. The use of SLS-I compound as jollows H₂SO₄, + KC₁₂H₂₅.S0₃ according to fixed proportion to permit dissolving almost all inclusions. the retained inclusion quantity was l'ery small smooth only about 1 µm. The result had been gained whole thin nickel plates.