EFFECT OF SURFACTANT ON FABRICATION OF CORE-SHELL STRUCTURED MESOPOROUS SILICA NANOPARTICLES

  • Ngoc Huyen Nguyen Thi
  • Xuan Thi Diem Trinh Nguyen
  • Nguyen Minh Thao
  • Ngoc Tram Nguyen Thi
Từ khóa: Core-shell structure, CTAB, HMSN, particle size, surfactant, TEOS

Tóm tắt

Hollow mesoporous silica nanoparticles (HMSN) were synthesized by the hard-template method, consisting of three stages: forming a solid silica nano core (SSN), developing a coreshell structure (SSN@CTAB-SSN), and etching the core to form hollow silica nanoparticles. This study evaluated the effect of surfactant (Cetyltrimethylammonium Bromide – CTAB) in the second stage on forming core-shell structured silica nanoparticles. Transmission electron microscopy (TEM) characterization showed that no core-shell structure formed when no surfactant was used, and the coating mechanism was clearly explained. SSN@CTAB-SSN particles were about 160.6 ± 0.8 nm, with the shell having a size of about 60 nm. The zeta potential and stability were measured by dynamic light scattering (DLS), which was +31.5 ± 0.7 mV.

điểm /   đánh giá
Phát hành ngày
2025-07-28
In ra
Tập. 25 Số. S1 (2025)
Chuyên mục
Bài viết